Computational Predictions of Hydrogen-assisted Fatigue Crack Growth

Abstract

A new model is presented to predict hydrogen-assisted fatigue. The model combines a phase field description of fracture and fatigue, stress-assisted hydrogen diffusion, and a toughness degradation formulation with cyclic and hydrogen contributions. Hydrogen-assisted fatigue crack growth predictions exhibit an excellent agreement with experiments over all the scenarios considered, spanning multiple load ratios, H2 pressures and loading frequencies. These are obtained without any calibration with hydrogen-assisted fatigue data, taking as input only mechanical and hydrogen transport material properties, the material’s fatigue characteristics (from a single test in air), and the sensitivity of fracture toughness to hydrogen content. Furthermore, the model is used to determine: (i) what are suitable test loading frequencies to obtain conservative data, and (ii) the underestimation made when not pre-charging samples. The model can handle both laboratory specimens and large-scale engineering components, enabling the Virtual Testing paradigm in infrastructure exposed to hydrogen environments and cyclic loading.

Funding source: The authors acknowledge financial support from TENARIS through the R&D project ‘‘A Virtual Platform to Assess the Integrity of HydrogenContaining Components’’. C. Cui acknowledges financial support from the UKRI Horizon Europe Guarantee MSCA Postdoctoral Fellowship (grant EP/Y028236/1). Emilio Martínez-Pañeda additionally acknowledges financial support from UKRI’s Future Leaders Fellowship programme [grant MR/V024124/1].
Countries: Italy ; United Kingdom
Loading

Article metrics loading...

/content/journal6135
2024-05-29
2024-11-21
/content/journal6135
Loading
This is a required field
Please enter a valid email address
Approval was a Success
Invalid data
An Error Occurred
Approval was partially successful, following selected items could not be processed due to error